Environment-friendly aluminum plastic film for lithium battery
An aluminum-plastic film, lithium battery technology, applied in secondary batteries, battery pack parts, circuits, etc., can solve the problems of exhaust gas, waste water discharge, difficult operation, complex process, etc., to achieve simple production process and stable product performance. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0020] A polyamide (PA) outer layer film (Cangzhou Mingzhu Company) with a thickness of 25 μm is produced by bidirectional stretching with a plastic extrusion salivating machine, and chemically modified polyvinyl alcohol with a thickness of 1 μm is coated on one side of a 40 μm aluminum foil with a coating machine (PVA) coating solution (Hebei Bairuier Company), on the other side of the aluminum foil coating thickness of 1 μm physically modified polyvinyl alcohol (PVA) coating solution (Hebei Bairuier Company), then the salivating polyamide ( PA) film, use a dry compound machine, use epoxy, phenolic resin adhesive, thickness 5μm (Jiangsu Bairuier Company) and aluminum foil coated with chemically modified polyvinyl alcohol (PVA) coating surface compound, the compounded semi-finished product is placed Put it into a curing chamber with a temperature set at 45°C for 48 hours.
[0021] Polypropylene (CPP) films with a thickness of 41 μm (Jiangsu Bairuier Co., Ltd.) were manufactured w
Embodiment 2
[0028] Manufacture polyester (PET) outer layer film (Jiangsu Shuangxing) with a thickness of 25 μm through two-way stretching with a plastic extrusion salivating machine, and use a coating machine to coat a chemically modified polyvinyl alcohol with a thickness of 1 μm on one side of an aluminum foil of 40 μm ( PVA) coating solution (Hebei Bairuier Company), on the other side of the aluminum foil coating thickness 1μm physical modification polyvinyl alcohol (PVA) coating solution (Hebei Bairuier Company), then pour the salivating polyester (PET ) film, use a dry compound machine, use epoxy, phenolic resin adhesive, thickness 5μm (Jiangsu Bairuier Company) and aluminum foil coated with chemically modified polyvinyl alcohol (PVA) coating surface compound, the compounded semi-finished product is put into Matured for 48 hours in a curing chamber set at 45°C.
[0029] A film with a thickness of 80 μm, which can be thermally bonded with polyvinyl alcohol (PVA) coating, is produced by a
PUM
Property | Measurement | Unit |
---|---|---|
Total thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap